Materials Properties

 

MATERIAL Thermal Conductivity (W/m°C) Thermal Dissipation (cm2/s) Yield Strength (Mpa) Specific Density (g/cm3) Elasticity (104Kg/cm) Tension Strength (Mpa) Elongation(%) Minimal Part Thickness (mm) Melting Temperature (°C) Strength/Weight Ratio Weight Ratio (%)
PC/ABS 0.91     1.14 2.4. 104/25 3/40 1.6 160/90 102/41 100
PC/GF (CF15%) +/- 0.2mm     1.34 4.9 60   1.26      
CFRP (CF30%)       1.5 14.0     0.89      
MG 79 0.38 160 1.8 47.0 280 8 0.59 470-596    
AL 100 0.36 160 2.7 67.0 315 3 0.53 555-615    
Steel 42   400 7.86   517 22   1250    
Zinc 113     6.6         377-432    
Iron       7.1              
Brass       8.5